*Please note – These are mixed colours, colour accuracy should be checked before application. No responsibility for colour differences can be accepted after use.
Two-pack acrylic base coat with direct adhesion on non ferrous metal substrates for solid, metallic and mica colours, in a two-coat process. To overcoat with glossy and matt acrylic clearcoat.
General industrial manufactured items.
- Fast drying
- Easy application
- Excellent adhesion on aluminium and its alloys, zama (zinc+aluminium+magnesium), brass and epoxy primers (a previous adhesion test is always recommended)
- Excellent light resistance
- Only metallic and mica colours of this basecoat can also be overcoated with soft-touch clearcoat
Aluminium and its alloys, mama (zinc+aluminium+magnesium), brass: degreasing with 00695 silicone remover slow followed by blowing.
Spray – Mixing ratio:
LS945 2K GRIP BASE (derived from binder 29945) 1000 parts
29355 LECHSYS ACRITOP STANDARD HARDENER 100 parts
00825 (Standard) -00824 (Slow) LECHSYS UNIVERSAL THINNERS 500 parts
Pot life at 20°C : 4 hours
Spray viscosity at 20 °C: 16-18” DIN 4
Recommended spray temperature: above 5°C under 30°C
Ø Air cap: 1,2 mm
Air pressure: 3,5 Atm
N° of coats: 2-3
Recommended film thickness: 20-30 μ
Theoretical coverage: 1 kg of mixture = 7.3 mÇ at 25 μ
1 l of mixture = 6.7 mÇ at 25 μ
V.O.C. of the mixture ready for use: ~ 750 g/l
Air drying at 20°C :
Overcoatable with clearcoat after 20 min.
Acrylic industrial clearcoats for a two-coat process:
96390 ACRIFAN CLEAR COACH
96598 ACRIPLAST CLEAR SEMIOPACA
09852 CERAMIC CLEAR
31575 CLEAR SOFT MATT TH only on metallic and mica colours, NOT on solid colours.